閱讀：169 發(fā)布時(shí)間：2022-3-24文獻(xiàn)名：Antibacterial, biological, and physicochemical properties of root canal sealers containing chlorhexidine-hexametaphosphate nanoparticles
作者： Nancy Kudsy Carvalhoa, Ana Flávia Almeida Barbosaa, Bárbara de Paula Coelhoa, Lúcio de Souza Gonçalvesc, Luciana Moura Sassonea, Emmanuel João Nogueira Leal Silvaab
a Department of Endodontics, School of Dentistry, State University of Rio de Janeiro (UERJ), Rio de Janeiro, RJ, Brazil
b Department of Endodontics, School of Dentistry, Grande Rio University (UNIGRANRIO), Rio de Janeiro, RJ, Brazil
c Department of Dentistry, Estácio de Sá University, Rio de Janeiro, RJ, Brazil
摘要：
Objective
The aim of this study was to evaluate the influence of the incorporation of chlorhexidine-hexametaphosphate nanoparticles (CHX-HMP NPs) on antibacterial, cytotoxic and physicochemical properties of AH Plus (AH), MTA Fillapex (MTA) and Pulp Canal Sealer (PCS).
Methods
The NPs were synthesized and characterized by Scanning Electron Microscopy (SEM), Dynamic Light Scattering (DLS), zeta potential, Atomic Force Microscopy (AFM) and Energy-Dispersive X-ray Spectroscopy (EDS). The incorporation was made by weight, 2% and 5% of NPs. The antimicrobial activity, cytotoxicity, flow, radiopacity, setting time, solubility and pH were evaluated. The statistical analysis was performed by two-way analysis of variance test and Tukey post hoc test (P < 0.05).
Results
SEM analysis showed the tendency for CHX-HMP NPs to cluster, the effective mean diameter measured by DLS: 169.39 nm and the zeta potential: -10.18 mV. The NPs were individually measured by AFM: 22.99–52.75 nm. EDS analysis identified the presence of C, N, O, Na, P, Cl. After incorporation: The Direct Contact Test showed an increase in the antimicrobial action of AH, PCS and MTA; the sealers showed a decrease in flow and at 24 h of immersion also an increase in solubility, but did not affect the radiopacity of the samples; AH setting time increased and MTA did not reach setting under any of the conditions tested. All samples showed a decrease in pH value as the immersion time progressed.
Significance
The incorporation of NPs can improve the antimicrobial performance of endodontic sealers without impairing other biological and physicochemical properties.
關(guān)鍵詞：Chlorhexidine; Nanoparticles; Root canal sealers