国产日产欧美精品-亚洲国产综合久久精品-色综合色国产热无码一-亚洲欧美日本国产,免费观看一区二区三区_在线观看片A免费不卡观看_亚洲а∨天堂久久精品_99久无码中文字幕一本久道

基于藍寶石襯底的全區(qū)域覆蓋的單層二硫化鎢返回列表頁

舉報評價

參考價: ￥ 6979.7

訂貨量: ≥1 片

具體成交價以合同協(xié)議為準(zhǔn)

產(chǎn)品型號

品牌2D Semiconductors

廠商性質(zhì)生產(chǎn)商

所在地泰州市

在線詢價加入對比查看聯(lián)系電話

更新時間：2024-06-03 19:24:38瀏覽次數(shù)：893次

聯(lián)系我時，請告知來自化工儀器網(wǎng)

產(chǎn)品分類品牌分類

二維材料: 鈣鈦礦/OLED 異質(zhì)結(jié) MOFS材料其他二維材料二維材料溶液二維材料薄膜二維材料粉末絕緣體黑磷六方氮化硼晶體碲化物晶體硒化物晶體硫化物晶體

全部產(chǎn)品列表

產(chǎn)品簡介

供貨周期	現(xiàn)貨	應(yīng)用領(lǐng)域	環(huán)保,化工,能源,綜合

This product contains full area coverage WS2 monolayers on c-cut sapphire substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick WS2 sheet.

詳情介紹

This product contains full area coverage WS2 monolayers on c-cut sapphire substrates. Sample size measures 1cm in size and the entire sample surface contains monolayer thick WS2 sheet. Synthesized full area coverage monolayer WS2 is highly luminescent and Raman spectroscopy studies also confirm the monolayer thickness.

Sample Properties.

Sample size	1cm x 1cm square shaped
Substrate type	(0001) c-cut sapphire
Coverage	Full coverage monolayer
Electrical properties	2.0 eV Direct Bandgap Semiconductor
Crystal structure	Hexagonal Phase
Unit cell parameters	a = b = 0.312 nm, c = 1.230 nm, α = β = 90, γ = 120°
Production method	Low pressure Chemical Vapor Deposition (LPCVD)
Characterization methods	Raman, photoluminescence, TEM, EDS

Specifications

1) Identification. Full coverage 100% monolayer WS2 uniformly covered across c-cut sapphire

2) Physical dimensions. One centimeter in size. Larger sizes up to 2-inch wafer-scale available upon requests.

3) Smoothness. Atomically smooth surface with roughness < 0.2 nm.

4) Uniformity. Highly uniform surface morphology. WS2 monolayers uniformly cover across the sample.

5) Purity. 99.9995% purity as determined by nano-SIMS measurements

6) Reliability. Repeatable Raman and photoluminescence response

7) Crystallinity. High crystalline quality, Raman response, and photoluminescence emission comparable to single crystalline monolayer flakes.

8) Substrate. c-cut Sapphire but our research and development team can transfer WS2 monolayers onto variety of substrates including PET, quartz, and SiO2/Si without significant compromisation of material quality.

9) Defect profile. WS2 monolayers do not contain intentional dopants or defects. However, our technical staff can produce defected WS2 using α-bombardment technique.

Supporting datasets [for 100% Full area WS2 coverage on c-cut Sapphire]

Transmission electron images (TEM) acquired from CVD grown full area coverage WS2 monolayers on c-cut sapphire confirming highly crystalline nature of monolayers

Energy dispersive X-ray spectroscopy (EDX) characterization on CVD grown full area coverage monolayer WS2 on c-cut sapphire confirming W:S 1:2 ratios

Room temperature photoluminescence spectroscopy (PL) and Raman spectroscopy (Raman) measurements performed on CVD grown full area coverage WS2 monolayers on c-cut sapphire. Raman spectroscopy measurement confirm monolayer nature of the CVD grown samples and PL spectrum display sharp and bright PL peak located at 2.00 eV in agreement with the literature.