当前位置：上海隆继金属集团有限公司>>技术文章>>UNS N08020镍基合金冷轧板标准
UNS N08020镍基合金
产品名称：ALLOY20/UNS N08020
国际通称：Alloy 20合金、UNS N08020、NS143、Inconel alloy20/NAS 335X、W.Nr.2.4460
Nicrofer 3620 Nb-alloy20、ATI 20
各国标准：ASTM B463/ ASME SB463、ASTM A240/ ASME SA240、ASTM B729/ ASME SB729
主要成分：
| Element | Wt, % |
|---|---|
| Carbon [C] | ≤0.07 |
| Manganese [Mn] | ≤2.00 |
| Phosphorus [P] | ≤0.045 |
| Sulfur [S] | ≤0.035 |
| Silicon [Si] | ≤1.00 |
| Nickel [Ni] | 32.00~38.00 |
| Chromium [Cr] | 19.00~21.00 |
| Molybdenum [Mo] | 2.00~3.00 |
| Copper [Cu] | 3.00~4.00 |
| Niobium+Tantalum [Nb+Ta] | 8xCarbon~1 |
| Iron | Remainder |
*The tabulated values are abstracted from ASTM B462 Gr. UNS N08020.
物理性能：
| Alloy | Tensile Strength, min. | Yield Strength, min. | Elongation, min. | Reduction of Area, min. | ||
|---|---|---|---|---|---|---|
| ASTM B462 | ksi | MPa | ksi | MPa | % | % |
| UNS N08020 | 80 | 551 | 35 | 241 | 30.0 | 50.0 |
*All values shall be measured at room temperature.
*Alloy 20 flanges shall be supplied in stabilized-annealed condition.
热处理：900-1150℃之间保温1-2小时，快速空冷或水冷。
机械性能：抗拉强度：σb≥550Mpa，屈服强度σb≥240Mpa：延伸率：δ≥30%，硬度；HB135-220
耐腐蚀性及主要使用环境：
Alloy 20合金具有很多优异性能的耐蚀合金，对氧化性和中等还原性腐蚀 有很好的抵抗能力，具有优异的抗应力腐蚀开裂能力和好的耐局部腐蚀能力在很多化工工艺介质中有满意的耐蚀特性。
有优异的抗应腐蚀开裂能力和好的耐局部还原性复合介质腐蚀，运用于硫酸环境及含有卤族离子及金属离子的硫酸溶液工业装置。
配套焊接材料及焊接工艺：Alloy 20合金的焊接建议采用AWS A5.14焊丝ERNiCrMo-3或AWS A5.11焊条ENiCrMo-3，焊接工艺及指导书欢迎来电索取。
应用领域有：硫酸酸洗设备、磷酸生产设备、石油化工装备、煤化工、海洋平台、海水淡化、复合板、波纹管膨胀节等行业和产品。